Method for thermally erasing information stored in an aluminum oxide data storage medium

ABSTRACT

The present invention provides methods and apparatuses for writing information to, reading information from, and erasing information on a luminescent data storage medium comprising Al 2 O 3 . The method includes writing and erasing of the information using photoionization via sequential two-photon absorption and non-destructive reading the information using fluorescent detection. The apparatuses for writing and reading the information incorporate confocal detection and spherical aberration correction for multilayer volumetric fluorescent data storage. The methods also allow multilevel recording and readout of information for increased storage capacity.

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application is a continuation-in-part of U.S. application Ser. No. 10/309,021, filed Dec. 4, 2002, entitled, “Aluminum Oxide Material for Optical Data Storage,” which claims the priority of U.S. Provisional App. No. 60/336,749, filed Dec. 4, 2001, now abandoned, and U.S. application Ser. No. 10/309,179, filed Dec. 4, 2002, entitled, “Method for Forming Aluminum Oxide Material Used in Optical Data Storage,” which claims the priority of U.S. Provisional App. No. 60/417,153, filed Oct. 10, 2002. The entire disclosures and contents of the above applications are hereby incorporated by reference.

BACKGROUND OF THE INVENTION

[0002] 1. Field of the Invention

[0003] The present invention relates to methods of writing to, reading from and erasing information on a data storage medium.

[0004] 2. Description of the Prior Art

[0005] Various attempts have been made to design higher density data storage media for computer devices to replace conventional storage media such as magnetic disks, CD-ROMs, DVDs, etc. Many of the obstacles faced with respect to developing improved data storage methods have been associated with inadequate storage material properties. For example, photopolymers have been investigated for use in one-bit or holographic data storage. However, photopolymers exhibit strong dimensional shrinkage. Also, most photo-sensitive polymers may be used only as WORM media (write once, read many times) and the rewritable photopolymers are still unstable and show significant fatigue when write-read cycles are repeated many times. Even write-once fluorescent photopolymers show strong reduction of fluorescent output signals when read repeatedly. An additional problem with most photopolymers, as well as for photorefractive crystals, another potential material for volumetric one-bit recording, is the necessity of using a femto-second high peak power Ti-sapphire laser to achieve efficient two-photon absorption. This type of laser is big, expensive and suitable only for laboratory demonstration.

[0006] Therefore, there exists a need for better materials for making high density data storage devices.

SUMMARY OF THE INVENTION

[0007] It is therefore an object of the present invention to provide a data storage method utilizing an aluminum oxide material that allows for fast electronic processing in comparison with phase change transition or photo-induced polymerization techniques for data storage.

[0008] It is a further object of the present invention to provide a data storage method utilizing an aluminum oxide material that is capable of achieving a write/read rate up to 100 Mbit per second.

[0009] It is yet another object of the present invention to provide a data storage method utilizing an aluminum oxide material that provides the ability to perform parallel processing of multiple marks on a data storage medium for an increase of write/read rate.

[0010] It is yet another object of the present invention to provide a data storage method utilizing an aluminum oxide material that provides high data storage density restricted only by diffraction limit and NA of the optical components.

[0011] It is yet another object of the present invention to provide a data storage method utilizing aluminum oxide material that provides the possibility of multilevel data storage due to dependency of fluorescence response from writing laser energy.

[0012] It is yet another object of the present invention to provide a data storage method utilizing aluminum oxide material that only requires low laser light energies for writing and reading of information (pJ and nJ range).

[0013] It is yet another object of the present invention to provide a data storage method utilizing aluminum oxide material that provides extremely high temperature and time stability of stored data.

[0014] It is yet another object of the present invention to provide a data storage method utilizing aluminum oxide material that provides no degradation of material performance after millions of write/read cycles.

[0015] According to a first broad aspect of the present invention, there is provided a method of writing information to a data storage medium comprising the steps of: providing a luminescent data storage medium comprising Al₂O₃; and writing the information to the luminescent data storage medium with an optical source.

[0016] According to a second broad aspect of the present invention, there is provided a method of reading information stored on a data storage medium comprising the steps of: exciting a luminescent data storage medium with an optical source to thereby cause the luminescent data storage medium to emit a fluorescent light signal, wherein the luminescent data storage medium comprises Al₂O₃ and wherein the optical source emits a read laser beam having a wavelength in the range of an absorption band of the luminescent data storage medium; and measuring the laser induced fluorescence light signal from the luminescent data storage medium, to thereby read the information stored on the luminescent data storage medium.

[0017] According to a third broad aspect of the present invention, there is provided a method of erasing information stored on a data storage medium comprising the steps of: providing a luminescent data storage medium comprising Al₂O₃, the luminescent data storage medium having the information stored thereon; and illuminating the luminescent data storage medium with an optical source to thereby erase the information.

[0018] According to a fourth broad aspect of the present invention, there is provided a method of writing information to a data storage medium comprising the steps of: providing a luminescent data storage medium comprising Al₂O₃; and writing the information to the luminescent data storage medium by using a two-photon absorption technique and a photo-ionization technique resulting in removal of an electron from a color center in the luminescent data storage medium and moving the electron to a thermally stable trap in the luminescent data storage medium.

[0019] According to a fifth broad aspect of the present invention, there is provided a method of reading information from a data storage medium comprising the steps of: exciting a luminescent data storage medium with an optical source having a wavelength in the range of an absorption band of the luminescent data storage medium to thereby cause the luminescent data storage medium to emit a fluorescent light signal, wherein the luminescent data storage comprises Al₂O₃ and color centers; and measuring the induced fluorescence signal from the luminescent data storage medium, to thereby read the information stored on the luminescent data storage medium, wherein the method is performed in a condition of one-photon absorption without photo-ionization of the color centers and results in excitation of the color centers by the optical source to thereby cause the color centers to emit the fluorescence signal.

[0020] According to a sixth broad aspect of the present invention, there is provided a method of erasing information stored in the data storage medium comprising steps of: providing a luminescent data storage medium comprising Al₂O₃, the luminescent data storage medium having the information stored thereon; and illuminating the luminescent data storage medium with an optical source in conditions of two-photon absorption to thereby erase the information.

[0021] According to a seventh broad aspect of the present invention, there is provided a apparatus comprising: a luminescent data storage medium comprising Al₂O₃; and an optical source for writing information to the luminescent data storage medium.

[0022] According to an eighth broad aspect of the present invention, there is provided a apparatus comprising: a luminescent data storage medium comprising Al₂O₃; a first optical source for exciting the luminescent data storage medium to thereby cause the luminescent data storage medium to emit a fluorescent light signal when information is stored on the luminescent data storage medium; and means for measuring the emitted fluorescent light signal.

[0023] According to a ninth broad aspect of the present invention, there is provided a apparatus comprising: a luminescent data storage medium comprising Al₂O₃; and writing means for writing information to the luminescent data storage medium by using a two-photon absorption technique and a photo-ionization technique resulting in removal of an electron from a color center in the luminescent data storage medium and moving the electron to a thermally stable trap in the luminescent data storage medium, the writing means comprising a first optical source.

[0024] Other objects and features of the present invention will be apparent from the following detailed description of the preferred embodiment.

BRIEF DESCRIPTION OF THE DRAWINGS

[0025] The invention will be described in conjunction with the accompanying drawings, in which:

[0026]FIG. 1 is a schematic diagram illustrating writing information to a data storage medium of the present invention using a two-photon absorption and reading information from a data storage medium of the present invention using laser-induced fluorescence with a confocal detection scheme;

[0027]FIG. 2 shows optical absorption spectra of two crystals: a known Al₂O₃:C crystal used in radiation dosimetry and an Al₂O₃:C,Mg single crystal according to a preferred embodiment of the present invention with a higher concentration of F⁺-centers (absorption at 255 nm) and new absorption bands corresponding to F₂ ⁺(2 Mg)— and F₂ ²⁺ (2Mg)-centers clearly distinguishing a new material;

[0028]FIG. 3 is a graph showing the absorption, excitation and emission spectra of F₂ ²⁺(2Mg)-centers created in Al₂O₃:C,Mg in an as-received or erased state, with an excitation spectrum of 520 nm emission band coinciding well with the absorption band at 435 nm assigned to the same defect, and showing the wavelength dependence of a two-photon photo-ionization cross-section for F₂ ²⁺(2Mg)-centers;

[0029]FIG. 4 is a graph showing a continuous readout of fluorescent signal at a 20 MHz repetition rate with the lifetime of F₂ ²⁺(2Mg)-center emission at 520 nm equal to 9±3 ns for an Al₂O₃:C,Mg luminescent material according to a preferred embodiment of the present invention;

[0030]FIG. 5 is a graph illustrating the multilevel data storage principle based on the proportionality between 435 and 335 nm absorption band intensity and the “write” time for a Al₂O₃:C,Mg luminescent material of a preferred embodiment of the present invention;

[0031]FIG. 6 is a graph showing the excitation and emission spectra of F₂ ⁺(2Mg)-centers obtained as a result of photo-conversion of an F₂ ²⁺(2Mg)-center (“write” operation) in Al₂O₃:C,Mg crystals using pulsed blue laser light with a wavelength of 430 nm;

[0032]FIG. 7 is a graph showing the lifetime measurement of F₂ ⁺(2Mg)-center emission at 750 nm equal to 80±5 ns for an Al₂O₃:C,Mg luminescent material according to a preferred embodiment of the present invention;

[0033]FIG. 8 is a graph showing quadratic dependence of a photo-ionization cross-section of F₂ ²⁺(2Mg)-centers on peak laser light intensity illustrating high probability of a two-photon absorption process in Al₂O₃:C,Mg crystals;

[0034]FIG. 9 is a wavelength dependence of photo-ionization cross-section showing an optimum wavelength at about 390 nm to perform “write” operation in Al₂O₃:C,Mg;

[0035]FIG. 10A is a graph showing temperature dependence of an optical absorption band at 255 nm (F⁺-centers) and illustrates high thermal stability of trapped charge up to 650° C.;

[0036]FIG. 10B is a graph showing temperature dependence of an optical absorption band at 335 nm (F₂ ⁺(2Mg)-centers) and illustrates high thermal stability of trapped charge up to 650° C.;

[0037]FIG. 10C is a graph showing temperature dependence of an optical absorption band at 435 nm (F₂ ²⁺(2Mg)-centers) and illustrating high thermal stability of trapped charge up to 650° C.;

[0038]FIG. 10D is a graph showing temperature dependence of an optical absorption band at 630 nm (F₂ ³⁺(2Mg)-centers) and illustrating high thermal stability of trapped charge up to 650° C.;

[0039]FIG. 11 is a band diagram illustrating electronic processes in an Al₂O₃ crystal doped with Mg impurity during “write” and “read” operations;

[0040]FIG. 12 is a fluorescent image of a matrix of 3×3 bits written in the XY plane of the crystal medium with 5 μm increments using CW 405 nm laser diode and read using a confocal detection scheme and 440 nm CW laser diode;

[0041]FIG. 13 is a 500×500 pixel image obtained in fluorescent contrast after writing 100×100 bits in the XY plane of the crystal with 1 μm increments in which bits were written with pulses of blue 411 nm laser diode and read with 440 nm laser diode;

[0042]FIG. 14 is a bit profile obtained in fluorescent contrast during X-scan of a crystal showing spatial resolution of the bits written with 15 nJ per bit and 1 μm incremental steps

[0043]FIG. 15 is a 400×400 pixel image obtained in fluorescent contrast in the XZ plane of the crystal after writing 3 bits in the X direction with 5 μm increments. Bits were written with pulses of blue 411 nm laser diode and read with 440 nm CW laser diode;

[0044]FIG. 16 is a 500×500 pixel image of 3 layers of bits obtained in fluorescent contrast in the XZ plane of the crystal after writing matrix of 7×3 bits with 5 μm increments in the X direction and 10 μm incremental motion in the Z direction in which bits were written with pulses of blue 411 nm laser diode and read with a 440 nm CW laser diode;

[0045]FIG. 17 is a graph demonstrating multilevel one-bit recording by measuring a fluorescent image during XY-scan of Al₂O₃ crystal in which 10 bits were written in the volume of the crystal with different numbers of 60 ps “write” laser pulses; and

[0046]FIG. 18 is a graph illustrating dependence of the modulation depth of bits as a function of number of “writing” laser pulses and demonstrating multilevel one-bit recording.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0047] It is advantageous to define several terms before describing the invention. It should be appreciated that the following definitions are used throughout this application.

Definitions

[0048] Where the definition of terms departs from the commonly used meaning of the term, applicant intends to utilize the definitions provided below, unless specifically indicated.

[0049] For the purposes of the present invention, the term “writing” refers to the conventional meaning of the term “writing” with respect to storing information on a data storage medium. In a preferred embodiment of the present invention, information is written to a data storage medium using a laser beam of one or more frequencies.

[0050] For the purposes of the present invention, the term “write position” refers to positioning a data storage medium to a position at which the data storage medium may be written to by a laser beam.

[0051] For the purposes of the present invention, the term “modulation depth of a fluorescent signal” refers to the parameter of the optical data storage system determined as the ratio of two fluorescent signals obtained from the same media spot before and after recording/writing.

[0052] For the purposes of the present invention the term “multilevel recording” refers to a method of writing information in a storage medium in which upon readout with a reading beam produces a readout value that may be digitized onto several discrete value levels representing more than one bit of digital information.

[0053] For the purpose of the present invention, the term “write time” refers to the time during which the writing beam is illuminating the spot on the medium to achieve desired change in the fluorescence signal amplitude (modulation depth of fluorescent signal). Such change in the fluorescence signal amplitude may be as low as 1% or as high as more than 90% depending on the desired modulation depth.

[0054] For the purposes of the present invention, the term “reading” refers to the conventional meaning of the term “reading” with respect to retrieving information stored on a data storage medium. In a preferred embodiment of the present invention, information is read from a data storage medium using a laser beam of one or more frequencies.

[0055] For the purposes of the present invention, the term “read time” refers to the time a specific storage location is illuminated by the read laser. The read time is equal to the read laser pulse length for stationary media and as a ratio of the reading spot size to the medium velocity for moving the medium.

[0056] For the purposes of the present invention, the term “erasing” refers to any of the conventional meanings of the term “erasing” with respect to digital data storage media. In general, erasing refers to restoring one or more sections of a data storage medium containing stored information to a state those sections had before having information stored in those sections.

[0057] For the purposes of the present invention, the term “physically erasing” refers to removing or destroying previously stored information on a data storage medium.

[0058] For the purposes of the present invention, the term “absorption band in the region of” or “emission band in the region of” refers to an absorption or emission band having a peak in the appropriate region. Sometimes the region may be a particular wavelength and sometimes the region may include a range of wavelengths indicating a possible shift in a band peak position.

[0059] For the purposes of the present invention, the term “crystalline material” refers to the conventional meaning of the term “crystalline material”, i.e. any material that has orderly or periodic arrangement of atoms in its structure.

[0060] For the purposes of the present invention, the term “luminescent material” refers to any of the conventional meanings of the term “luminescent material”.

[0061] For the purposes of the present invention, the term “data storage medium” refers to a medium upon which data may be stored, generally in digital form.

[0062] For the purposes of the present invention, the term “luminescent data storage medium” refers to a data storage medium that is comprised in part or in its entirety of a luminescent material.

[0063] For the purposes of the present invention, the term “defect” refers to the conventional meaning of the term “defect” with respect to the lattice of a crystal, i.e. a vacancy, interstitial, impurity atom or any other imperfection in a lattice of a crystal.

[0064] For the purposes of the present invention, the term “oxygen vacancy defect” refers to a defect caused by an oxygen vacancy in a lattice of a crystalline material. An oxygen vacancy defect may be a single oxygen vacancy defect, a double oxygen defect, a triple oxygen vacancy defect, or a more than triple oxygen vacancy defect. An oxygen vacancy defect may be associated with one or more impurity atoms or may be associated with an interstitial intrinsic defect such as misplaced interstitial oxygen atoms. Occupancy of an oxygen vacancy by two electrons gives rise to a neutral F-center, whereas occupancy of any oxygen vacancy by one electron forms an F⁺-center. An F⁺-center has a positive charge, with respect to the lattice. A cluster of oxygen vacancy defects formed by double oxygen vacancies is referred to as an F₂-type center. A cluster of oxygen vacancy defects formed by two F⁺-centers and charge-compensated by two Mg-impurity atoms is referred to as a F₂ ²⁺(2Mg)-center.

[0065] For the purposes of the present invention, the term “F-type center” refers to any one of the following centers: F-center, F⁺-center, F₂ ⁺-center, F₂ ⁺⁺-center, F₂ ⁺(2 Mg)-center, F₂ ⁺⁺(2Mg)-center, etc.

[0066] For the purposes of the present invention, the term “color center” refers to the conventional meaning of the term “color center”, i.e. a point defect in a crystal lattice that gives rise to an optical absorption of a crystal and upon light excitation produces a photon of luminescence. A color center, an impurity or an intrinsic defect in a crystalline material creates an unstable species. An electron localized on this unstable species or defect performs quantum transition to an excited state by absorbing a photon of light and performs quantum transition back to a ground state by emitting a photon of luminescence. In a preferred embodiment of the present invention, color centers are present in a concentration of about 10¹³ cm⁻³ to 10¹⁹ cm⁻³.

[0067] For the purposes of the present invention, the term “luminescence lifetime” or “fluorescence lifetime” refers to a time constant of an exponential decay of luminescence or fluorescence.

[0068] For the purposes of the present invention, the term “wide emission band” refers to an emission band that has full width at half maximum bigger than 0.1 eV and is a result of strong electron-phonon interaction. One example of a wide emission band is the wide emission band around 520 nm.

[0069] For the purposes of the present invention, the term “charge-compensated” refers to a defect in a crystal lattice that electrostatically compensates the electrical charge of another defect. For example, in a preferred embodiment of the present invention, Mg and C impurities may be used to charge-compensate one oxygen vacancy defect, two oxygen vacancy defects, a cluster of these defects, etc. comprising F₂ ²⁺(2Mg)-centers.

[0070] For the purposes of the present invention, the term “two-photon absorption or 2 PA” refers to a quantum mechanical process of light absorption by a color center when two photons have been absorbed simultaneously or sequentially by the localized electron of the color center and the electron makes a quantum transition into an excited state or a conduction band of the crystal.

[0071] For the purposes of the present invention, the term “one-photon absorption or 1 PA” refers to a quantum mechanical process of light absorption by a color center when only one photon has been absorbed by the localized electron of the color center and the electron makes a quantum transition into an excited state without having been transferred to a conduction band of the crystal.

[0072] For the purposes of the present invention, the term “laser light power density” or “laser light intensity” refers to a physical quantity measured as an average light energy of the laser beam propagating through the medium per second and divided by the area of laser beam waist.

[0073] For the purposes of the present invention, the term “substantially insensitive to room light” refers to a crystalline material that does not change significantly its coloration or concentration of electrons on traps (concentration of unstable species) under ambient light conditions.

[0074] For the purposes of the present invention, the term “capable of being used for long-term data storage” refers to a crystalline material that does not change significantly its coloration or concentration of electrons on traps (concentration of unstable species) at ambient temperatures.

[0075] For the purposes of the present invention, the term “photo-ionization cross-section” refers to a parameter having a dimension of cm²/J that determines how much light energy per unit area is required to perform photo-ionization of a color center. The larger the photo-ionization cross-section means less energy per unit area is required to perform ionization (recording of the bit).

[0076] For the purposes of the present invention, the term “fluorescence yield” refers to the parameter determined as a ratio of the number of photons emitted by a luminescent material to the number of photons absorbed by this luminescent material.

[0077] For the purposes of the present invention, the term “electron trap” refers to a structural defect in a crystal lattice able to create a localized electronic state and capable of capturing free electrons from a conduction band of the crystalline material.

[0078] For the purposes of the present invention, the term “hole trap” refers to a structural defect in a crystal lattice able to create a localized electronic state and capable of capturing free holes from a conduction band of the crystalline material.

[0079] For the purposes of the present invention, the term “deep trap” refers to an electron or hole trap having a thermal activation energy larger than kT, where T is absolute temperature of the crystal and k is Boltzmann's constant.

[0080] For the purposes of the present invention, the term “efficient deep trap” refers to a deep trap which is capable of trapping electrons or holes and which has a sufficient capture cross-section.

[0081] For the purposes of the present invention, the term “multilevel optical data storage” or “multivalued optical data storage” refers to the ability of the data storage system to perform recording and reading of data from the same physical location in the medium with a number of quantized data or signal levels more than two.

[0082] For the purposes of the present invention, the term “confocal detection” refers to a method of optically detecting a fluorescence signal in which the focal plane inside the medium of the optical read/write head is optically re-imaged onto a plane which contains an aperture or set of apertures having size comparable to or smaller than the diffraction limited spot size of the projected spot of fluorescent data storage medium.

[0083] For the purposes of the present invention, the term “spherical aberration compensation (SAC)” refers to a technique for compensating or correcting the spherical aberration that arises when a high numerical aperture objective (of NA of at least 0.35) is focused to a different depth inside the volume of the storage medium. The spherical aberration correction allows to maintain diffraction limited spot size over larger depth of the medium, preferably larger than 500 microns, via dynamically changing the focusing lens properties depending on the depth of the focus inside the medium achieving diffraction limited spot size at the focusing depth.

Description

[0084] The need for high capacity and high transfer rate computer devices for massive data storage has stimulated a search for new types of media that are able to exist in two or more stable configurations. By transferring the storage medium from one configuration into another, one may write and erase the bit of information, whereas by analyzing the configuration of the medium, the reading of the bit is realized. A large number of materials and techniques have been suggested for data storage and data processing, but only a few of these techniques have found a practical application. Because of the large number of requirements, it is extremely difficult to develop a medium for optical data storage devices, which preferably meets all these requirements. The following articles, the contents and disclosures of which are hereby incorporated by reference, describe several of the techniques that have been attempted: International Symposium on Optical Memory and Optical Data Storage 2002, Technical Digest Publication of IEEE, Catalog #02EX552 (July 2002); Optical Data Storage 2001, Proceedings of SPIE, Vol. 4342 (2001); Optical Data Storage 2000, Proceedings of SPIE, Vol. 4090 (2000); International Symposium on Optical Memory and Optical Data Storage 1999, SPIE, Vol. 3864 (1999); Advanced Optical Data Storage: Materials, Systems, and Interfaces to Computers, Proceedings of SPIE, Vol. 3802 (1999); and K. Schwartz, The physics of optical recording, Springer-Verlag, Germany (1993), the entire contents and disclosures of which are hereby incorporated by reference.

[0085] Some of the most important requirements that data storage devices preferably meet are: an ability to repeatedly write, read, and erase the data (>10⁶ cycles); a high density of bits per unit volume or area (>10¹¹ cm⁻³); a high data transfer rate (>10⁷ bit/s); a minimum access time (<10⁻² s); a long lifetime for the storage medium (>10 years) and non-volatility of the information stored in the storage medium; an environmental stability of medium characteristics; safety of the stored data; and an ability to accomplish data error correction.

[0086] Several methods have been attempted to provide storage devices that might be able to compete with or replace conventional magnetic induction methods to achieve desirable characteristics. Among the methods attempted have been to use: magneto-optic and electro-optic effects (Pockels effect, Kerr effect, Faraday effect, photorefractive effect, etc.), the photochromic effect in dye polymers and inorganic crystals, and phase transformation in the storage medium at the spot being heated with a laser beam. Some of these methods have been successfully realized in the form of phase change media in the form of CD-RW and DVD-RW, and magneto-optical WREM discs and drives that are already on the market. Other methods, such as near-field, solid immersion lens recording, and atomic force microscopy are merely contemplated, see Alternative Storage Technologies Symposium 2001, Monterey California, Jun. 26, 2001, the entire contents and disclosure of which is hereby incorporated by reference.

[0087] Most of the conventional techniques mentioned above that use 2D (thin film) media are approaching a fundamental limit of storage density caused by a minimum achievable focused laser light spot or in the case of magnetic recording by thermal instabilities of magnetic domain walls (super paramagnetic effect). The most promising way to overcome these limitations may be to use volumetric (3D-space) recording. Among 3D types of data storage, the types of data storage that have been investigated, most have been in the area of digital holography, see Holographic data storage, (eds.: H. J. Coufal, D. Psaltis, G. Sincerbox), Springer 2000, p. 488, and volumetric multilayer single-bit recording, see Confocal and Two Photon Microscopy, Foundations, Applications, and Advances, (ed. Alberto Diaspro) Wiley-Liss, 2002, p. 567; the entire contents and disclosures of the above references are hereby incorporated by reference.

[0088] Several kinds of materials, such as photopolymers, photochromic materials and photorefractive crystals, have been proposed as possible recording media with a confocal detection scheme when one bit in the volume of the medium may be written as a local refractive index change using two-photon absorption (2 PA) of a high peak-power short pulse laser beam and the recorded data is read by measuring the change in reflection of the read laser light, see U.S. Pat. No. 5,289,407 to Strickler, et al.; James H. Strickler, Watt W. Webb, Three-dimensional optical data storage in refractive media by two-photon point excitation, Optics Letters, Volume 16, Issue 22, 1780, November 1991; Y. Kawata, H. Ishitobi, S. Kawata, Use of two-photon absorption in a photorefractive crystal for three-dimensional optical memory, Optics Letters, Volume 23, Issue 10, 756-758, May 1998; A. Toriumi, J. M. Herrmann, S. Kawata, Nondestructive readout of a three-dimensional photochromic optical memory with a near-infrared differential phase-contrast microscope, Optics Letters, Volume 22, Issue 8, 555-557, April 1997; M. Ishikawa, Y. Kawata, C. Egami, O. Sugihara, N. Okamoto, M. Tsuchimori, O. Watanabe, Reflection-type confocal readout for multilayered optical memory, Optics Letters, Volume 23, Issue 22, 1781-1783, November 1998; A. Toriumi, S. Kawata, M. Gu, Reflection confocal microscope readout system for three-dimensional photochromic optical data storage, Optics Letters, Volume 23, Issue 24, 1924-1926, December 1998; Min Gu, Daniel Day, Use of continuous-wave illumination for two-photon three-dimensional optical bit data storage in a photo-bleaching polymer, Optics Letters, Volume 24, Issue 5, 288-290, March 1999; Yoshimasa Kawata, Takuo Tanaka, Satoshi Kawata. Randomly accessible, multilayered optical memory with a Bi₁₂SiO₂₀ crystal, Applied Optics-IP, Volume 35, Issue 26, 5308-5311, September 1996; Daniel Day, Min Gu, Andrew Smallridge, Use of two-photon excitation for erasable rewritable three-dimensional bit optical data storage in a photo-refractive polymer, Optics Letters, Volume 24, Issue 14, 948-950, July 1999; Y. Shen, J. Swiatkiewicz, D. l Jakubczyk, F. Xu, P. N. Prasad, R. A. Vaia, B. A Reinhardt, High-Density Optical Data Storage With One-Photon and Two-Photon Near-Field Fluorescence Microscopy, Applied Optics, Volume 40, No. 6, 938-940, February 2001; T. Wilson, Y. Kawata, S. Kawata, Readout of Three-Dimensional Optical Memories, Optics Letters, Volume 21, No. 13, 1003-1005, July 1996; H. Ueki, Y. Kawata, S. Kawata, Three-Dimensional Optical Bit-Memory Recording and Reading With a Photorefractive Crystal: Analysis and Experiment, Applied Optics, Volume 35, No. 14, 2457-2465, May 1996; Min Gu, Confocal Readout of Three-Dimensional Data Bits Recorded by the Photorefractive Effect Under Single-Photon and Two-Photon Excitation, Proceedings of the IEEE, Volume 87, No. 12, 2021-2029, December 1999, the entire contents and disclosures of which are hereby incorporated by reference.

[0089] One-bit micro-holograms were suggested as the way to increase bit reflectivity and signal-to-noise and carrier-to-noise ratio (SNR and CNR, respectively), see U.S. Pat. No. 6,322,931 to Cumpston, et al.; U.S. Pat. No. 6,322,933 to Daiber, et al.; H. J. Eichler, P. Kuemmel, S. Orlic, A Wappelt, High-Density Disk Storage by Multiplexed Microholograms, IEEE Journal of Selected Topics in Quantum Electronics, Volume 4, No. 5, 840-848, September/October 1998; Y. Kawata, M. Nakano, Suk-Chun Lee, Three-Dimensional Optical Data Storage Using Three-Dimensional Optics, Optical Engineering, Volume 40, No. 10, 2247-2254, October 2001, the entire contents and disclosures of which are hereby incorporated by reference.

[0090] Several types of photochromic materials have been proposed for 3D one-bit optical data storage: organic fluorescent dyes dispersed in a polymer matrix, which undergo chemical or structural conformation, diffusion and polymerization as a result of illumination. Two-photon absorption in fluorescent photopolymers and confocal detection schemes have also been used, see U.S. Pat. No. 5,325,324 to Rentzepis, et al.; D. A. Parthenopoulos and P. M. Rentzepis, Three-Dimensional Optical Storage Memory, Science, Vol. 245, pp. 843-845, 1989; Daniel Day, Min Gu, Effects of Refractive-Index Mismatch on Three-Dimensional Optical Data-Storage Density in a Two-Photon Bleaching Polymer, Applied Optics-IP, Volume 37, Issue 26, 6299-6304, September 1998; Mark M. Wang, Sadik C. Esener, Three-Dimensional Optical Data Storage in a Fluorescent Dye-Doped Photopolymer, Applied Optics, Volume 39, No. 11, 1826-1834, April 2000; E. P. Walker, X. Zheng, F. B. McCormick, H. Zhang, N.-H. Kim, J. Costa, A. S. Dvornikov, Servo Error Signal Generation for 2-Photon Recorded Monolithic Multilayer Optical Data Storage, Optical Data Storage 2000, Proceedings of SPIE Vol. 4090, pp. 179-184, 2000; H. Zhang, A. S. Dvornikov, E. P. Walker, N.-H. Kim, F. B. McCornick, Single Beam Two-Photon-Recorded Monolithic Multi-Layer Optical Disks, Optical Data Storage 2000, Proceedings of SPIE, Vol. 4090, pp. 174-178, 2000; Y. Zhang, T. D. Milster, J. Butz, W. Bletcher, K. J. Erwin, E. Walker, Signal, Cross Talk and Signal to Noise Ratio in Bit-Wise Volumetric Optical Data Storage, Technical Digest of Joint International Symposium on Optical Memory and Optical Data Storage, IEEE Catalog, No. 02EX552, pp.246-248, 2002; E. P. Walker, W. Feng, Y. Zhang, H. Zhang, F. B. McCormick, S. Esener, 3-D Parallel Readout in a 3-D Multilayer Optical Data Storage System, Technical Digest of Joint International Symposium on Optical Memory and Optical Data Storage, IEEE Catalog, No. 02EX552, pp. 147-149, 2002; and Ingolf Sander (Constalation 3D, Inc.) Fluorescent multilayer technology, In: Alternative Storage Technologies Symposium 2001, Monterey Calif., Jun. 26, 2001, the entire contents and disclosures of which are hereby incorporated by reference.

[0091] Using luminescent materials as data storage media is especially attractive because of their ability to realize multilevel (or multivalued) optical data storage. Luminescent response is proportional to the product of the energy deposited in the medium during “writing” and “reading”. If the concentration of defects undergoing electronic transition in the volume corresponding to one bit of information is large enough, then that element of the light-sensitive medium may be used in a “gray scale” mode and the optical data storage system may be used as a multilevel (or multivalued) data storage system. The potential storage capacity is increased proportionally to the number of data levels reliably achieved. The total linearity of luminescent response may stretch over several orders of magnitude. Different logical states of the medium may be represented by different intensities of the luminescent signal and digitized using thresholding electronic circuits. In practice, 10 levels of fluorescent intensity may be achieved by changing the energy or the time duration of the laser “writing” beam. An increased density of data storage is one of the main potential advantages of the luminescent techniques of the present invention.

[0092] Similar approaches to writing to and reading from a data storage medium have been demonstrated in silver-doped photoluminescent glasses used in radiation dosimetry, see B. Lommler, E. Pitt, A. Scharmann, Optical creation of radiophotoluminescence centers in dosimeter glass by two-photon absorption, Radiat. Prot. Dosim. Vol. 65, No. 1-4, pp.101-104 (1996), the entire contents and disclosure of which is hereby incorporated by reference. Two-photon UV excitation (“writing”) produces a photoluminescence signal that may be repeatedly “read” with the same laser, but at lower power, without measurable erasure of information. However, how such data may be “erased” without heating the medium is not clear. Complications may also be caused by the long-term process of diffusion and luminescent center transformation that lead to a “build-up” of luminescent signal.

[0093] A promising way to overcome the limitations of conventional data storage systems is to use volumetric or 3D recording. Among 3D-technologies, multilayer one-bit recording with two-photon absorption (2 PA) has some clear advantages. The probability of two-photon absorption is proportional to a square of laser light intensity. Two-photon absorption allows one to perform photo-ionization or photo-transformation of a photosensitive medium only in the vicinity of a tightly focused laser beam without affecting the surrounding volume of the material. The size of one three-dimensional bit or voxel written using 2 PA may be made as small as 1×1×3 μm. Extremely high storage density of up to 10 Tbits/in³ is expected.

[0094] An apparatus built according to the present invention is illustrated by FIG. 1, described in more detail below. Two lasers based on blue laser diodes are used to write and to read the data from a storage medium. Two-photon absorption from a more powerful CW laser having a shorter wavelength is used for recording the data. High NA of the objective lens allows for the high intensity of the laser light needed for 2 PA to be achieved and for the formation of a diffracted limited recorded bit size. One-photon-induced fluorescence induced by low energy and longer wavelength laser and a confocal detection scheme may be used for reading the data Confocal detection allows one to significantly reduce cross-talk between adjacent bits, tracks, and layers with the purpose of achieving a desirable signal-to-noise ratio (SNR).

[0095] An important objective of the present invention is to provide a method and apparatus that performs writing operation using high probability of 2 PA and makes the reading operation non-destructive by decreasing the probability of 2 PA during the readout. At the same time the method and apparatus according to the present invention use 1 PA and laser-induced fluorescence during readout at a highest possible level needed to achieve acceptable SNR and high data transfer rate.

[0096] Most of the problems with the various storage media described above have been related to inadequate material properties. Most of the photopolymers suggested for one-bit or holographic data storage show high sensitivity but exhibit strong dimensional shrinkage. Most of the photo-sensitive polymers may be used only as WORM media (write once, read many times), whereas rewritable photopolymers are still unstable and show significant fatigue when write-read cycles are repeated many times. Even write-once fluorescent photopolymers show strong reduction of fluorescent output signals when read repeatedly. An additional obstacle for most suggested photopolymers and photorefractive crystals tested for volumetric one-bit recording is a necessity of using a femto-second high peak power Ti-sapphire laser to achieve efficient two-photon absorption, because a Ti-sapphire laser is big, expensive and at the time are suitable mostly for laboratory demonstration.

[0097] Therefore, utilization of an efficient and stable inorganic photochromic fluorescent material for one-bit optical recording and reading is an objective of the present invention.

[0098] The low thermal energy depth of the traps responsible for capturing electrons produced by ionization with the laser light during writing causes thermally stimulated release of electrons from traps at ambient temperatures and fading of the stored data. This is generally not acceptable, especially for multivalued storage, which requires precise digitization of the analog luminescent signal. Furthermore, the chemical instability of some luminescent materials and their sensitivity to oxidization and humidity when contacted with air require the use of protective layers. In some organic fluorescent materials, dimensional stability is a significant problem because of material shrinkage as a result of photochemical transformation and polymerization.

[0099] Electronic transitions in solids caused by light excitation with relaxation times on the order of 10⁻¹² to 10⁻⁹ s are fundamentally very fast and are considered among the most promising quantum systems for massive optical data storage. Luminescence decay time after a pulse of laser stimulation determines the time needed for retrieval of each bit of information and the maximum achievable data transfer rate.

[0100] To achieve more stable and reliable data storage and optical processing, one should use chemically, mechanically and thermally stable luminescent materials with deep traps and luminescent centers. To produce such deep centers, one needs to use a wide gap dielectric. Furthermore, these “thermally” and “optically” deep traps require a shorter wavelength of laser light for excitation (“writing”), stimulation (“reading”) and restoration (“erasing”). For optical recording, the minimum light spot diameter is equal to: d≈0.5λ/NA, where NA is the numerical aperture of the optical head. Therefore, blue and UV lasers have a clear advantage against IR lasers for achieving higher storage densities. The latest developments in blue and UV solid state lasers, based on heterostructures of wide gap semiconductors like GaAlN create a real possibility for use of materials with wide energy gaps.

[0101] The low energy depth of the traps responsible for the accumulation of the charge carriers leads to the thermally stimulated release of electrons at ambient temperatures and to fading of the stored data. This is not acceptable, especially for multilevel data storage, which requires precise digitizing of the analog luminescent signal. Furthermore, the chemical instability and sensitivity to oxidization and humidity when contacted with air require the use of protection layers.

[0102] Corundum or sapphire (α-Al₂O₃) is an important technological material in many optical and electronic applications. It is used as a host material for solid-state lasers, as optical windows, as a substrate material in semiconductor epitaxial growth and, more recently, as a radiation detector see M. S. Akselrod, V. S. Kortov, D. J. Kravetsky, V. I. Gotlib, Highly Sensitive Thermoluminescent Anion-Defective α-Al2O3:C Single Crystal Detectors, Radiat. Prot. Dosim., Vol. 32(1), pp.15-20 (1990). In spite of excellent dosimetric properties of carbon-doped Al₂O₃ with oxygen vacancies, the luminescent centers in this material (F-centers) have a very long luminescence lifetime (35 ms). However, α-Al₂O₃ is unacceptable for fluorescent one-bit recording applications requiring a high data transfer rate. Known Al₂O₃ materials also do not have absorption bands that may undergo photochromic transitions suitable for volumetric data storage applications.

[0103] With respect to the new Al₂O₃ crystalline material described in U.S. application Ser. No. 10/309,021, filed Dec. 4, 2002, and U.S. application Ser. No. 10/309,179, filed Dec. 4, 2002, the entire contents and disclosures of which are hereby incorporated by reference, important features of this material utilized in the present invention are the electronic and optical properties of a storage phosphor and its defect structure. The Al₂O₃:C,Mg crystalline material has color centers absorbing light, stable traps of electrons and holes and its luminescent centers have a short luminescence lifetime.

[0104] A simplified scheme illustrating how the crystalline fluorescent material may be used in an optical data recording and retrieving drive is illustrated by FIG. 1. In scheme 100, a 405 nm “write” laser beam 102 and 440 nm “read” laser beam 104 are produced by two diode lasers 106 and 108, respectively. Laser beams 102 and 104 are directed on a single crystalline disk 110 made of Al₂O₃:C,Mg through a flipping mirror 112, dichroic mirror 114, and a high NA focusing objective lens 116. Disk 110 spins as shown by arrow 118 or moves by a 3D translation stage represented by arrows 119. An optical pick-up head that combines objective lens 116, dichroic mirror 114, focusing lens 120, a confocal pinhole 122, and a photodetector 124 slides along the radius of the disk 110. Selection of the focal depth of the bit 126, a certain data layer within 3D volume of the disk and correction of spherical aberrations are performed by moving an additional optical component of an optical pick-up head (not shown). A photodetector 124 is used to monitor laser-induced fluorescence 128 during writing and reading. A green fluorescence 126 is collected by objective lens 116, reflected by the dichroic mirror 114, focused by lens 120 on confocal pinhole 122, and detected by a photon counter or a digital oscilloscope 130 interfaced with a computer 132.

[0105] In the scheme shown in FIG. 1, two-photon absorption during a “write” operation allows for very tight localization of the photo-ionization process in the focal spot of the laser beam and 3D confinement of the written bit (green fluorescence 126). One-photon excitation of the fluorescent light from the medium using “read” laser light of a longer wavelength and a confocal fluorescence detection scheme allows one to perform non-destructive reading of bits multiple times.

[0106] The method described in the present invention is made possible due to the unique optical properties of Al₂O₃:C,Mg. The primary information storage process in Al₂O₃ is photo-ionization, followed by the subsequent capture of the excited electronic charge by trapping centers. Thus, for the efficient storage of information, it is necessary that Al₂O₃ crystals contain both light absorbing color centers and defects capable of trapping electrons. High quantum yield of fluorescence is also required for one-bit confocal recording. According to a preferred embodiment of the present invention volumetric recording of bits is performed using 2 PA, whereas non-destructive reading operation utilizes 1 PA and fast laser induced fluorescence.

[0107] The Al₂O₃ crystalline materials produced according to a method described in U.S. application Ser. No. 10/309,021, filed Dec. 4, 2002, and U.S. application Ser. No. 10/309,179, filed Dec. 4, 2002, the entire contents and disclosures of which are hereby incorporated by reference, and utilized in the present invention include several types of oxygen vacancy defects and are doped with carbon and magnesium impurities and can be grown by those skilled in the art using any conventional crystal growth method (for example using the Czochralski method). The crystalline material utilized in the present invention is characterized by several optical absorption (OA) bands: at 205, 230, 255, 335, 435, and 630 nm (FIG. 2). The blue absorption band at 435 nm is responsible for the visible green coloration of the crystal. One important feature of the new aluminum oxide material is a high concentration of single and double oxygen vacancies in the form of neutral F-centers as well as F⁺ and F₂ ²⁺ centers, charge-compensated by the nearby Mg-impurity atoms.

[0108] An F⁺-center is an oxygen vacancy with one electron charge-compensated by one Mg²⁺-ion and is denoted as an F⁺(Mg)-center. This center is characterized by at least two absorption bands at 230 and 255 nm (FIG. 2) and has a luminescence band at 330 nm with a lifetime of less than 5 ns. A cluster of two of these defects forms an aggregate vacancy defect composed of two F⁺-centers and two Mg-impurity atoms. This aggregate defect with two localized electrons, denoted here as F₂ ²⁺(2Mg), is favorable for optical data storage. It is responsible for a blue absorption-excitation band at 435 nm (FIG. 3), produces a green fluorescence band at 520 nm, and has a short lifetime equal to 9±3 ns (FIG. 4).

[0109] Exposure of an Al₂O₃:C,Mg crystal having oxygen vacancy defects to high intensity laser light of appropriate wavelength results in conversion of the same structural defect from one charged state into another. For example, F₂ ²⁺(2Mg)-centers are converted into F₂ ⁺(2Mg)-centers with 430 nm illumination (FIG. 5) and may be converted back with 335 nm pulsed laser light. After photochromic transition induced by blue laser light, Al₂O₃:C,Mg crystals exhibit an absorption/excitation band at 335 nm (FIGS. 5 and 6), a broad fluorescent emission at 750 nm (FIG. 6) with relatively fast decay time equal to 80±10 ns (FIG. 7).

[0110] In a preferred embodiment of the present invention a two-photon absorption (2 PA) process is utilized for recording the information in the volume of Al₂O₃:C,Mg. Usually 2 PA is considered as a process of simultaneous absorption by the luminescence center of two photons. The sum of energies of these two photons is preferably enough to perform excitation of the luminescent center whereas energy of only one photon is not sufficient for the excitation transition. 2 PA in that case is performed through the virtual (non-existing) quantum energy state of defect and the probability of it is very low. To perform 2 PA, femto- or picosecond laser pulses with a power density on the order of 100 MW/cm² are required. A very important trait of Al₂O₃:C,Mg, which enables so-called “sequential” 2 PA, is that defects absorbing the laser light and producing the fluorescence have an excited state located deep in the energy gap. The lifetime of this excited state is sufficiently long to significantly increase the probability of a second photon absorption needed for photo-ionization and data recording. At the same time the lifetime of the excited state for this color center is short enough to allow fast reading of a fluorescent signal with a high data transfer rate.

[0111] The evidence of preferred two-photon absorption in aggregate oxygen vacancy defects is provided by quadratic dependence of the photo-ionization cross-section of these centers versus laser light intensity (see FIG. 8). Photo-ionization cross-section for the 2 PA process is inversely proportional to the decay constant and directly proportional to the product of the absorption cross-sections of the ground and excited states. Wavelength dependence of photo-ionization cross-section of F₂ ²⁺(2Mg) centers is shifted to a shorter wavelength in comparison with the 1 PA band (FIGS. 3 and 9) and is another indication of the 2 PA process in Al₂O₃:C,Mg crystals.

[0112] Erasing of written data and restoration of original optical absorption (coloration) and fluorescence of the storage medium according to the present invention can be achieved optically or thermally. Al₂O₃:C,Mg crystalline material includes deep traps of charge. These deep traps of charge have a delocalization temperature about 600° C. to 700° C. and have a concentration about 10¹³ to 10¹⁷ cm⁻³. The delocalization temperature of these deep traps was found from the optical absorption experiment (see FIGS. 10A, 10B, 10C and 10D) with step annealing of the Al₂O₃:C,Mg crystal after it was illuminated with a 430 nm pulsed laser light that is equivalent to a “write” operation in the optical data storage system. Optical absorption bands of F⁺-centers at 255 nm and F₂ ²⁺ (2Mg)-centers at 435 nm increase their intensities and restore their original intensity in the temperature region between 600 and 700° C. The opposite trend may be seen in the same temperature range for 335 nm band of F₂ ⁺(2Mg)-centers and 630 nm band of F₂ ³⁺(2Mg)-centers indicating that these centers convert into F₂ ²⁺(2Mg)-centers during annealing. 630 nm absorption band of F₂ ³⁺(2Mg)-centers appears only after “write” operation with the pulsed blue laser light and is not visible in the absorption spectrum of the fresh Al₂O₃:C,Mg crystal shown in FIG. 2.

[0113] Optical erasure of recorded bits by reverse photochromic transformation and restoration of the 435 nm absorption band and 520 nm fluorescence can be achieved according to another preferred embodiment of the present invention using sequential illumination of the Al₂O₃:C,Mg crystal with 205±30 and 335±30 nm laser light corresponding to absorption bands of F and F₂ ⁺(2Mg) centers. Illumination with the light at 205±30 nm corresponding to an F-absorption band performs photo-ionization of F-centers and generates free electrons. These free electrons can be captured by the defects ionized during recording. In particular these electrons are captured by deep hole traps and F₂ ²⁺(2Mg) and F₂ ³⁺(2Mg)-centers. The goal of one of the preferred embodiments of the present invention is to convert as many double oxygen vacancy defects as possible into a F₂ ⁺(2Mg) charge state. These defects are characterized by an intensive absorption band in the region of 335 nm. Ionization of F centers can be performed by either coherent laser light or incoherent light, produced for example by deuterium of xenon lamps. Subsequent illumination of the crystal with the high power density laser light having 335±30 nm performs 2 PA on F₂ ⁺(2Mg) centers, converts them into F₂ ²⁺(2Mg)-centers. The described optical procedure restores a 435 nm absorption band and 520 nm fluorescence characteristic to these defects and restores original green coloration of the Al₂O₃:C,Mg crystal.

[0114] Preferred electronic processes during “write” and “read” operation in the utilized Al₂O₃:C,Mg material of the present invention are explained using a band diagram as in FIG. 11. A preferred doped Al₂O₃ material of the present invention for use as a data storage medium may be formed to contain a high concentration of trapping sites and fluorescent centers with precisely desirable characteristics. Data storage media generally exist in at least two stable physical states assigned correspondingly to “0” and “1” states. An initial configuration (logical 0 state) of as-received or erased Al₂O₃ medium has a high concentration of F₂ ²⁺(2Mg)-centers, characterized by an intensive absorption band in the region of 435±5 nm.

[0115] By illumination with the writing laser light (“write” beam”) of the appropriate photon energy hν₁ (or wavelength λ₁) and intensity, which is high enough to ionize the above described crystal defects, one may produce free electrons to be trapped in pre-existing electronic defects. The traps in Al₂O₃:C,Mg are deep enough to keep the charge carriers for a long time at ambient temperature without being thermally released. This second state of a quantum system is now in a metastable “charged” configuration (logical “1” state). To “read” the state of the medium, the stimulation light of the same as writing light or another photon energy hν₂ (or wavelength λ₂) is applied and fluorescent photon of energy hν₃ (or wavelength λ₃) is detected. In case of fluorescent one-bit recording, a written bit produces reduced fluorescence intensity whereas an unwritten spot produces original intensive fluorescence.

[0116] Electronic defects in wide gap dielectrics like Al₂O₃ are characterized by the energy levels of their ground and excited states. If the excited state of the electronic defect is located close or within the conduction band, the defect may be ionized by one-photon absorption. A different situation takes place when the excited state is located deep within the energy gap of the crystal. Absorption of one photon corresponding to the energy transition between ground and excited states of the electronic defect results in a localized transition followed by non-radiative and radiative decay (fluorescence). This one-photon absorption process is nondestructive and may be used for reading information.

[0117] To remove an electron from such a deep defect and to change the luminescent properties of the particular defect in the crystal, simultaneous absorption of two photons is used in the present invention. The first absorbed photon excites the electron of the above described electronic defect into its excited state, whereas the second photon transfers the electron from the above described excited state within the energy gap into the conduction band. An electron in the conduction band is now delocalized (removed from its original defect site) and may be trapped by another defect.

[0118] Writing the data may be performed (see FIG. 11) using two-photon absorption of 435±40 nm blue laser light by the F₂ ²⁺(2Mg)-centers described above. The first photon excites one of the two electrons localized on the center to its excited state while the second photon performs the second transition between the excited state and the conduction band, thus performing photo-ionization of the center. The final stage of the writing process is localization (or trapping) of the above described photoelectron by another defect, namely by another F₂ ²⁺(2Mg)-center, or by F⁺(Mg)-center or by carbon impurity. The result of these photochromic transformations is (a) creation of another charged state of the aggregate defect, F₂ ⁺(2Mg)-center, having three localized electrons and characterized by a UV absorption band at 335 nm, or (b) creation of a neutral F-center with a UV absorption band at 205 nm, or a carbon related trap responsible for 190° C. TL peak. All three processes result in formation of optically deep and thermally stable electronic states and may be used in a preferred embodiment of the present invention for long-term data storage. The first process (a) has a higher probability that was determined from the efficiency of photo-conversion of optical absorption bands. As a result of photo-ionization, an F₂ ²⁺(Mg)-center converts into F₂ ³⁺(Mg) that has an absorption band at 620 nm and the released electron is trapped by another F-₂ ²⁺(Mg)-center converting it into an F₂ ⁺(Mg)-center having three localized electrons and characterized by an absorption band at 335 nm and an emission band at 750 nm.

[0119] The present invention provides two types of fluorescent processes for reading data (see FIG. 11). The Type 1 or “negative” process involves stimulation of original green fluorescence of F₂ ²⁺(2Mg)-centers using blue laser light excitation at 435±40 nm. The intensity of this excitation is preferably significantly reduced to avoid two-photon absorption, but sufficient to generate green fluorescence enough for the reliable detection of information. Small volumes of Al₂O₃ crystal (voxels) subjected to two-photon ionization during writing show reduced or no fluorescence, whereas the unwritten voxels show high intensity of green fluorescence.

[0120] A type 2 readout process of the present invention, the so-called, “positive” readout process, involves using laser excitation at 335±30 nm to stimulate the fluorescence of F₂ ⁺(2Mg)-centers created during recording. The intensity of this excitation also is preferably significantly reduced to avoid two-photon absorption. The intensity of fluorescence of F₂ ⁺(2Mg)-centers in the region of 750 nm having an 80 ns lifetime is used as a measure of data during a “readout” process for binary or multilevel data storage.

[0121] Writing the data on the aluminum oxide medium of the present invention using 2 PA and reading of data from the same medium may be performed by means of laser induced fluorescence (LIF) and is preferably achieved through electron motion and electronic transitions. No phase transformation or other structural changes happen during “write” or “read” operations. This makes the data recording and retrieving processes extremely fast and reproducible.

[0122] A process of writing data according to a preferred embodiment of the present k invention will now be described. First the data storage medium in the form of a Mg-doped anion-deficient Al₂O₃ single crystal is moved to a desired position with respect to the diffraction limited laser “write” beam, focused on a predetermined depth of the medium by means of mechanical motion of the medium and/or the adjustable components of the optical head. Spherical aberration compensation of the focused laser beam is also performed at this stage by means of mechanical motion of the optical component or by electro-optical component based for example on liquid crystal phase shifter.

[0123] Then, the data storage medium is illuminated with the above-described focused beam of writing laser light having wavelength λ₁ for the period of time equal to a write time t₁. The above described “write” wavelength λ₁ is in the range of 370-490 nm with a more preferred wavelength equal to 390 nm. The sequential two-photon absorption process described in the present invention can be achieved at laser intensity of higher than 1 kW/cm². The “write” time is in the range of 0.1 ps to 1 ms with a more preferred time equal to 10 ns. The result of the writing operation is ionization and photo-conversion of F₂ ²⁺(2Mg)-centers into F₂ ³⁺(2Mg)-centers:

F₂ ²⁺(2Mg)+2hν ₁=F₂ ³⁺(2Mg)+e ⁻

[0124] Electrons released from F₂ ²⁺(2Mg)-centers as a result of the photo-ionization process are captured by deep traps and other nearby F₂ ²⁺(2Mg)-and F⁺-centers:

F₂ ²⁺(2Mg)+e=F₂ ⁺(2Mg)

F⁺(Mg)+e ⁻=F(Mg)

[0125] The above-described deep trapping sites are able to store information almost indefinitely.

[0126] The present invention provides three preferred modes of reading data using a confocal laser induced fluorescent detection scheme. The first mode reads the data with the same laser beam of wavelength λ₁ used for “writing”, but with significantly reduced intensity and time of illumination to avoid two-photon absorption and erasure of stored data. In the second mode of operation, the reading laser beam has a wavelength λ₂ longer than λ₁, but it is still within the absorption band of F₂ ²⁺(2Mg)-centers. For example, wavelength λ₂ is selected to be 460 nm. A longer wavelength further reduces the probability of 2 PA and allows for higher laser light intensity for excitation of fluorescence and provides better signal-to-noise ratio (SNR). These two modes of “read” operation utilize a fluorescent emission band of F₂ ²⁺(2Mg)-centers in the region of 520 nm (FIG. 3). Lifetime of this fluorescence is 9±2 ns (FIG. 4) and is fast enough to achieve a 100 Mbit/s data transfer rate. A strong fluorescence signal corresponding to a 0 binary state indicates that no “write” operation was performed on the particular bit.

[0127] These two first modes of reading may be referred to as “negative” types of operation. The third mode of reading operation utilizes fluorescence of F₂ ⁺(2Mg)-centers (three electrons occupying the aggregate defect) created as a result of trapping the electron by the F₂ ²⁺(2Mg)-centers during writing operation:

F₂ ²⁺(2Mg)+e ⁻=F₂ ⁺(2Mg)

[0128] F₂ ⁺(2Mg)-centers may be excited in their absorption band in the region of 335 nm or in F⁺-center absorption band at 255 nm. Emission of these centers is in the infrared region and is in the region of 750 nm (see FIG. 6 for details of excitation and emission spectra). The lifetime of the 750 nm emission is 80±10 ns (see FIG. 7) and is short enough for a data transfer rate up to 10 Mb/s.

[0129] A preferred reading operation of the present invention will now be described. First, the above described data storage medium is moved to a desired position with respect to a focused “read” laser beam. The above-described read laser beam has a wavelength λ₂ is in the range of 390-500 nm with a more preferred wavelength equal to 460 nm. Then, the above described data storage medium is illuminated with the above described focused beam of “read” light for the period of time equal to a “read” time t₂. The above described “read” time t₂ is in the range of 0.1 ns to 1 ms with the more preferred time in the range between 2 and 15 ns most preferred time equal to 5 ns. The laser-induced fluorescence produced by the Al₂O₃ data storage medium is then measured using a photodetector. The above-described LIF is the “data” light at the third wavelength λ₃ in the region of 750 nm and is in the range from 620 nm to 880 nm. The above-described fluorescent signal is then processed to obtain the value of the stored data.

[0130] In another preferred embodiment of the present invention fluorescence intensity from the recorded bit is inversely proportional to the amount of energy (or number of “write” laser pulses) delivered to the bit during the recording stage (FIGS. 17 and 18). It can be digitized for binary or multilevel types of data and thus can be used for further increase of density of data storage.

[0131] The present invention also allows parallel processing of multiple marks on the storage medium for further increase of “write” or “read” rate and data storage density. Parallel processing is one of the main advantages of optical data recording. One may use one-dimensional or two-dimensional arrays of lasers and photo-detectors (CCD chips or CMOS detectors).

[0132] The storage medium of the present invention also provides thermal, temporal and environmental stability of the medium and stored data. The common problem for fluorescent and photorefractive data storage medium is the thermal instability and result in thermal erasure of stored information. Al₂O₃ doped with carbon and magnesium exhibits extremely good thermal and temporal stability of information stored as electrons trapped on localized states formed by oxygen vacancy defects in the crystal structure. Lifetime of the charge carriers on traps depends on storage temperature. The higher the temperature, the smaller the lifetime. The deeper the traps—the longer the storage time. Most of the trapped electrons are associated with a 650° C. trap that has extremely high thermal and optical depth. Al₂O₃ crystals are very mechanically, chemically and optically stable and do not show degradation of performance for years. It was also shown that the recorded data is not erased by conventional room light illumination and the medium does not require light protection.

[0133] In another preferred embodiment of the present invention, the utilized method of optical data storage is capable of being used for long-term data storage.

[0134] In another preferred embodiment of the present invention, the utilized method of data recording requires laser energy of as small as 15 nJ per bit of information stored in the material.

[0135] In another preferred embodiment of the present invention, the utilized Al₂O₃:C,Mg crystalline material is substantially insensitive to room light in both written and erased states.

[0136] Compared with known technologies for optical data storage, the present invention provides several advantages. Utilization of fundamentally very fast electronic processes vs. comparatively slow phase change transitions and photo-induced polymerization for well known techniques provides a data transfer rate for one channel of up to 100 Mb/s. High data storage density is achieved due to 3D capability of the proposed materials and confocal detection schemes restricted only by the blue laser light diffraction limit and NA of the optical head. Multiple data layers may be accessed in the bulk of the medium during writing and reading operations using two-photon absorption techniques and confocal detection schemes. Non-volatile reading is achieved using one-photon excitation of fluorescent centers causing no degradation of stored information. Multilevel (multivalue) data storage may further increase data storage density due to linearity of luminescent response. Low average laser light intensities required for “writing” and “reading” of information (mW range) allows one to preferably use compact blue laser diodes. Well-established and efficient crystal growth technology produces Al₂O₃ crystals of high optical quality.

[0137] The present invention will now be described by way of example. The example experiments described below are meant to be illustrative of the material and procedure described above and should not be considered to be definitive descriptions of the invention.

EXAMPLE I

[0138] An optical data storage apparatus of the type illustrated in FIG. 1 was used for demonstrating the methods of the present invention. Both “write” and “read” laser beams were produced by respective semiconductor lasers built using Nichia laser diodes. Two types of writing lasers were tested: CW modulated laser from Power Technology, producing 18 mW of power at 405 nm and a PicoQuant pulsed laser, generating 1.5 mW at 411 nm (20 MHz, 60 ps pulse duration, 400 mW of peak power). Power of the “read” laser (440 nm, 3 mW) from Power technology was controlled using neutral density filters. The two laser beams were directed on the Al₂O₃:C,Mg crystalline storage media through a flipping mirror, dichroic mirror and a Nikon CFI PLAN FLUOR (0.85 NA, 60×) objective lens. This infinity conjugate objective lens has an optical component for manual spherical aberration compensation.

[0139] A single crystal disk of Al₂O₃:C,Mg was attached to the Polytec PI combined 3D stepper-piezo translation stage having 10 nm resolution. Selection of the focal depth or a certain data layer within 3D volume of the disk and correction of spherical aberrations was performed by moving the crystal 110 in the Z-direction and by rotating the correcting collar on the objective lens. The laser-induced fluorescence was collected by the objective lens and was reflected by the dichroic mirror through a focusing lens on the confocal pinhole. Long-pass yellow glass filter OG-515 134 was installed in front of the PMT to reject the residual blue laser light. Fluorescence detected by the photomultiplier tube was processed either by the digital oscilloscope or by the Stanford Research SR430 multichannel photon counter interfaced with a computer.

[0140] Recording of diffraction-limited bits at the different depth of Al₂O₃ crystal requires careful spherical aberration compensation (SAC). SAC of the optical system was calibrated using knife-edge technique with a specially made sapphire wedge having a thickness variation from 50 to 300 nm. After the proper focal plane position and optimum SAC were determined, both “write” and “read” laser beam profiles were measured. The diameter of a focused laser beam at 1/e² is equal to 0.55±0.05 μm for a 100 to 240 μm sapphire depth range.

EXAMPLE II

[0141] An Al₂O₃:C,Mg crystal plate 1.8 mm thick was cut from a crystal boule 45 mm in diameter. It was polished on both sides and installed in the test stand, described in the Example I, perpendicular to the optical axis of the objective lens with the crystal optical c-axis parallel to the polarization of the laser beam. The concentration of color centers responsible for the blue absorption band at 435 nm and green luminescence at 520 nm was estimated to be 17,000 centers per cubic micron.

[0142] The test was performed in the following sequence. The “write” operation was done using either modulated CW or pulsed laser diodes controlled by the computer interface board. Both types of lasers gave similar results, but the pulsed laser requires less energy per bit and produces better spatial resolution. The crystal medium was moved in the XY plane in step increments using piezo-actuators. During readout the crystal medium is translated in a ramp mode in X direction and with the step-increments in Y and Z directions. The CW laser beam (15 μW, 440 nm) excited green (520 nm) fluorescence from the crystal medium.

[0143] A high density data storage process for Al₂O₃:C:Mg utilizing two-photon absorption during one-bit recording and confocal fluorescent detection scheme for reading is illustrated by the image of FIG. 12. The bit image in fluorescent contrast was obtained using the method described in the present invention and was performed using an apparatus described above in the Example I and depicted in FIG. 1 in the following sequence. The “write” operation was done with a 405 nm diode laser beam at full power and the laser pulse duration was controlled with TTL pulses from the computer interface board. Decay of the fluorescent signal during writing operation was detected by the PMT and the oscilloscope and it was an indication of the successful writing. During reading operations, a CW low power blue diode laser (0.1 mW, 440 nm) modulated by another sequence of TTL pulses from a computer was used and green fluorescence separated by the dichroic mirror and the confocal pinhole was detected by the PMT and the photon counter.

[0144] Matrix of 3 by 3 bits spaced 5 μm apart was recorded and read as an image in fluorescent contrast (see FIG. 12). Nine bits were written with 405 nm laser light and with recording energy of just 25 nJ per bit. The “read” operation was performed by scanning of the recorded area of the crystal storage medium with the modulated CW laser diode having a wavelength at 440 nm that is longer than that of the “write beam” to prevent erasure of the information. To obtain the image of the written bits, scanning of the storage medium was performed with piezo-actuated 3D stage from Polytec PI. The single photon pulses of the fluorescent signal were detected using PMT and a Stanford Research SR430 multichannel photon counter interfaced with a personal computer. Scanning of the crystal was performed at 0.2 μm increments and with a 153 μm/s scan rate. The modulation depth of the recorded bits was about 40% and a full width at half maximum for a single bit was equal to about 1 μm.

EXAMPLE III

[0145] High density recording utilizing the method and the apparatus described in Example I was demonstrated. A 100×100 bit image with 1 μm increments in the X and Y directions (FIG. 13) was written using the 3D piezo-actuator. Each bit was written with 15 nJ of energy produced by pulsed PicoQuant diode laser (1000 pulses per bit). Reading of the bit pattern in fluorescent contrast was performed with a modulated CW-laser beam (440 nm, 15 μW) by scanning a raster with 200 nm between lines. An image having 500×500 pixels was obtained. Spatial profile of several bits spaced 1 μm apart is shown in FIG. 14 and demonstrates a 12% modulation depth.

EXAMPLE IV

[0146] Single bits written using 2 PA in the volume of Al₂O₃:C,Mg have different dimensions in lateral and axial direction with respect to the laser beam propagation direction. Theoretically axial size of the bit should be 3 to 5 times bigger than lateral bit size. To determine the size of the bits written in Al₂O₃:C,Mg in the axial direction (XZ plane), bits of data were written using a step increment motion of the 3D translation stage in XY plane, as described above in Example III, and then the image of the bits in fluorescent contrast was obtained by scanning the crystal in the XZ plane (FIG. 15). In yet another test, three layers of recorded bits were obtained at an average depth of 100 μm inside the crystal with a 17 μm separation between layers (FIG. 16). Each layer of bits was recorded and read with manual spherical aberration compensation (SAC) of the objective lens, which explains some distortion of the fluorescent image. Automated SAC should allow one to obtain up to 100 layers of data bits in the volume of the crystal having 2 mm in thickness with 2D equivalent of 10 Gbit/cm² of data storage density or close to 1 Tbit of data per disk having surface area equal to 100 cm².

EXAMPLE V

[0147]FIGS. 17 and 18 illustrate the test of multilevel data storage utilizing the Al₂O₃:C,Mg optical storage medium. The multilevel recording is based on the inverse proportionality between the fluorescent intensity of the written bits and the number of writing pulses. Ten bits were written in the Al₂O₃:C,Mg crystal with incremental number of “writing” laser pulses. Modulation depth of the produced bits is a nonlinear function of the number of laser pulses but nevertheless can be digitized onto several data values and even further increase the density of data storage utilizing the method and the medium of the present invention.

EXAMPLE VI

[0148] The optical properties of Al₂O₃:C,Mg crystals utilized in the tests of the present invention now will be described. Al₂O₃:C,Mg crystals in the shape of a boule having a 45 mm diameter were obtained. Crystals were then cut in to 1.8 mm thick disks and polished on both sides to obtain optical quality surfaces. Optical absorption spectra of the Al₂O₃:C,Mg crystalline material utilized in the present invention and of a known Al₂O₃:C crystal were obtained using Shimadzu UV-2104PC spectrophotometer and are shown in FIG. 2. The intensity of F⁺-bands at 230 and 255 nm is significantly higher in Mg-doped crystals. That indicates higher concentration of F⁺-centers, charge compensated by the Mg²⁺-ions. A blue absorption band at 435 nm indicates the creation of aggregate F₂ ²⁺(2Mg) defects used in the present invention. The grown crystal had 30 cm⁻¹ of absorption in the F-center band at 205 nm and an absorption coefficient of 10 cm⁻¹ in the F⁺-centers absorption band at 255 nm and 1.2 cm⁻¹ of absorption at 435 nm corresponding to absorption of F₂ ²⁺(Mg)-center (see FIG. 2). All absorption coefficients are presented after subtraction of the background pedestal. According to Smacula's formula, an absorption coefficient may be converted into a concentration of F-centers equal to 8.6·10¹⁷ cm⁻³ and concentration of F⁺-centers equal to 2.6·10¹⁷ cm⁻³ and 1.7·10¹⁶ cm⁻³ of F₂ ²⁺(Mg)-centers. The later number indicates that there are 17,000 fluorescent centers per cubic micron of a storage medium.

EXAMPLE VII

[0149] To justify the appropriate wavelength range of excitation and emission light, the emission-excitation spectra of aggregate centers in Al₂O₃ doped with Mg and C in two different states were obtained (FIG. 6 and FIG. 8). The spectra were obtained using a spectrofluorimeter equipped with the pulsed EG&G Xe-lamp, two scanning Acton Research spectrographs and a cooled CCD from Princeton Instruments. It was shown that a fresh (or erased) crystal shows an intense green luminescence band in the region of 520 nm with the excitation band corresponding to the blue absorption band at 435 nm (FIG. 2). After a writing operation with 440 nm pulsed laser, the blue 435 nm absorption band (see FIG. 5) and the green emission (see FIG. 6) disappears almost completely and the crystal shows an intensive emission band in the region of 750 nm with excitation bands at 255 nm and 335 nm (FIG. 8) assigned to F₂ ⁺(2Mg)-centers. Both emission bands: green band at 520 and IR band at 750 nm corresponding to F₂ ²⁺(2Mg)— and F₂ ⁺(2Mg)-centers have a short lifetime of about 9 and 83 ns respectively (see FIGS. 4 and 7).

EXAMPLE VIII

[0150] Photo-induced transformation of color centers in Al₂O₃:C,Mg utilized for recording and erasing the data was demonstrated. Exposure of an Al₂O₃:C,Mg crystal having oxygen vacancy defects to high intensity laser light of appropriate wavelength results in photo-induced conversion of the same structural defect from one charged state into another. For example, F₂ ²⁺(2Mg)-centers are converted into F₂ ⁺(2Mg)-centers with 430 nm illumination (FIG. 5) and may be converted back with 335 nm pulsed laser light. After photochromic transition induced by blue laser light, Al₂O₃:C,Mg crystals exhibit an absorption/excitation band at 335 nm (FIGS. 5 and 6), and a corresponding broad fluorescent emission at 750 nm (FIG. 6).

EXAMPLE IX

[0151] The evidence of preferred two-photon absorption in aggregate oxygen vacancy defects is provided by quadratic dependence of the photo-ionization cross-section of these centers versus laser light intensity (see FIG. 8). The test was performed with 415 nm, 4.5 ns laser pulses of an optical parametric oscillator illuminating a thin, 380 μm, Al₂O₃:C,Mg crystal and recording the decay constant of fluorescence as a function of laser energy density. The photo-ionization cross-section was than calculated as inversely proportional to this decay constant.

[0152] Wavelength dependence of a photo-ionization cross-section of F₂ ²⁺(2Mg) centers was measured as a function of wavelength. The peak position of a photo-ionization cross-section is shifted to a shorter wavelength in comparison with the one-photon absorption/excitation band (FIGS. 3 and 9) and is another indication of the 2 PA process in Al₂O₃:C,Mg crystals.

EXAMPLE X

[0153] A non-destructive readout utilizing one-photon absorption and fluorescent detection scheme was tested. A “write” operation was performed on Al₂O₃:C,Mg crystal using Continuum Panther Optical Parametric laser system. The laser system was tuned to generate a signal beam at 430 nm with the pulse duration of 4.5 ns and 60 μJ/mm² of energy density per pulse at the sample location. Reading of the written areas using Type 1 (or so-called “negative” operation) was performed with the blue laser diode from PicoQuant (0.6 mW of average power, 60 ps pulses, and the repetition rate of 20 MHz). Fluorescence at 520 nm was detected using a long pass glass filter OG515, high-speed ThorLabs DET210 silicon photo-detector and Tektonix TDS-3054 oscilloscope. A fluorescent signal with decay time of 9 ns is presented in FIG. 4 and indicates the possibility to achieve a data transfer rate of up to 100 Mbit/s. The fluorescent signal of unwritten area of the crystal show intensive 520 nm fluorescence. The amplitude of this pulsed signal did not show any decrease for several hours indicating that there is only one-photon absorption during “read” operation. For comparison, area of the crystal subjected to “writing” pulsed 435 nm laser light shows fluorescent signal equal to only 10% of the signal from unwritten crystal.

EXAMPLE XI

[0154] Readout operation utilizing a Type 2 or “positive” fluorescent process was tested. The “write” operation was performed using the same crystal sample as described in Example II and the same laser system described in Example IX. Reading of the written areas using Type 2 (or “positive” type of operation) was performed with the 335 nm UV beam from the same OPO laser system (100 nJ/pulse, 4.5 ns pulse duration and 10 Hz repetition rate). Fluorescence at 750 nm was detected using a long pass glass filter RG610 and a silicon photodiode DET-110 from ThorLabs, Inc. and Tektonix TDS-3054 oscilloscope. A fluorescent signal with decay time of 80±10 ns is presented in FIG. 7. An infrared fluorescence band at 750 nm of a bleached (written) crystal (see FIG. 6) has a longer lifetime than 520 nm green fluorescence of an erased crystal medium but it is still fast enough for the data transfer rate operation of up to 10 Mb/s.

EXAMPLE XII

[0155]FIG. 5 can be used as another illustration of multilevel data storage capabilities of the utilized optical storage medium based on the inverse proportionality between 435 and 335 nm absorption band intensity as a function of writing time using 430 nm writing beam. The Al₂O₃:C,Mg crystal produced according to the Example I was subjected to an incrementing number of 430 nm “writing” laser pulses of the OPO laser system described in Example V. Each second of illumination corresponds to 10 laser pulses. Absorption at a 435 nm band associated with the 520 nm fluorescent signal reduces as a function of number of writing laser pulses whereas the absorption of a 335 nm band associated with F₂ ⁺(2Mg) and infrared luminescence at 750 nm increases at the same time.

EXAMPLE XIII

[0156] A very important feature of photochromic transformations in Al₂O₃:C,Mg crystals is their high thermal stability. This high thermal and optical stability of recorded information is attributed to deep traps created during crystal growth and is demonstrated by a step-annealing test of optical absorption bands in Al₂O₃:C,Mg crystal (FIG. 10). During recording with high intensity blue laser light, 430 nm bands convert into 335 nm and 630 nm bands [2F₂ ²⁺(2Mg)+2hν→F₂ ⁺(2Mg)+F₂ ³⁺(2Mg)]. Reverse transformation of optical absorption bands [F₂ ⁺(2Mg)+F₂ ³⁺(2Mg)→F₂ ²⁺(2Mg)] takes place at about 650° C.

[0157] The same reverse photochromic transformation and restoration of the 435 nm absorption band was achieved by either pulsed 335±20 nm illumination or more efficient by sequential illumination of the crystal with 215 nm and than with 335 nm laser light corresponding to absorption of F and F₂ ⁺(2Mg) centers. An original strong absorption at 435 nm and fluorescence at 520 nm was restored. The inverse photochromic process that converts F₂ ⁺(Mg)-centers into F₂ ²⁺(Mg)-centers can be performed by two-photon absorption of laser light within 335 nm absorption band. Complete restoration of original green coloration of Al₂O₃:C,Mg can be achieved by heating the crystal to 650° C.

[0158] All documents, patents, journal articles and other materials cited in the present application are hereby incorporated by reference.

[0159] All documents, patents, journal articles and other materials cited in the present application are hereby incorporated by reference.

[0160] It is important to emphasize that the invention is not limited in its application to the detail of the particular material and technological steps illustrated herein. The invention is capable of other embodiments and of being practiced or carried out in a variety of ways. It is to be understood that the phraseology and terminology employed herein is for the purpose of description and not of limitation.

[0161] Although the present invention has been fully described in conjunction with the preferred embodiment thereof with reference to the accompanying drawings, it is to be understood that various changes and modifications may be apparent to those skilled in the art. Such changes and modifications are to be understood as included within the scope of the present invention as defined by the appended claims, unless they depart therefrom. 

1-77. Cancel
 78. A method of erasing information stored on a data storage medium comprising the steps of: (a) providing a luminescent data storage medium comprising Al₂O₃, said luminescent data storage medium having said information stored thereon; and (b) thermal annealing said luminescent data storage medium at a temperature of about 600 to 700° C. to thereby erase said information on said luminescent data storage medium.
 79. The method of claim 78, wherein step (b) comprises annealing said data storage medium at a temperature of about 650° C.
 80. The method of claim 78, further comprising the step of: cooling said luminescent data storage medium to room temperature.
 81. The method of claim 78, wherein at least part of the said luminescent data storage medium is a single crystal Al₂O₃ material.
 82. The method of claim 78, wherein said luminescent data storage medium comprises: a base material comprising Al₂O₃; a first dopant comprising magnesium; and a second dopant comprising carbon, wherein said luminescent data storage medium includes a plurality of at least one type of oxygen vacancy defect.
 83. The method of claim 82, wherein said luminescent data storage medium includes color centers having 335 and 630 nm optical absorption bands and a 750 nm fluorescent emission band prior to step (b), and wherein said color centers having 335 and 630 optical absorption bands are converted by step (b) into color centers having a 435 nm optical absorption band and a fluorescent emission band at 520 nm.
 84. The method of claim 82, wherein said Al₂O₃:C,Mg crystal has a green coloration and has original concentration of F₂ ²⁺(2Mg)-centers prior to said information being stored on said luminescent data storage medium, and wherein step (b) comprises restoring said green coloration and said original concentration of F₂ ²⁺(2Mg)-centers.
 85. An apparatus for erasing information stored on a data storage medium comprising: a luminescent data storage medium comprising Al₂O₃, said luminescent data storage medium having said information stored thereon; and annealing means for thermal annealing said luminescent data storage medium at a temperature of about 600 to 700° C. to thereby erase said information on said luminescent data storage medium.
 86. The apparatus of claim 85, further comprising cooling means for cooling said thermally annealed data storage medium to room temperature.
 87. The apparatus of claim 85, wherein at least part of the said luminescent data storage medium is a single crystal Al₂O₃ material
 88. The apparatus of claim 85, wherein said luminescent data storage medium comprises: a base material comprising Al₂O₃; a first dopant comprising magnesium; and a second dopant comprising carbon, wherein said luminescent data storage medium includes a plurality of at least one type of oxygen vacancy defect.
 89. The apparatus of claim 88, wherein said luminescent data storage medium includes color centers having 335 and 630 nm optical absorption bands and a 750 nm fluorescent emission band while said information is stored on said luminescent data storage medium, and wherein said color centers having 335 and 630 optical absorption bands are converted into color centers having a 435 nm optical absorption band and a fluorescent emission band at 520 nm by annealing said luminescent data storage medium at a temperature of about 650° C.
 90. The apparatus of claim 89, wherein said Al₂O₃:C,Mg crystal has a green coloration and has original concentration of F₂ ²⁺(2Mg)-centers prior to said information being stored on said luminescent data storage medium, and wherein said annealing means is capable of restoring said green coloration and said original concentration of F₂ ²⁺(2Mg)-centers. 